Perovskite solar cells could be improved by atomic-scale redesign
Perovskites shown great promise for making flexible, cheap solar cells. Except for one major snag – they degrade rapidly in natural conditions, greatly decreasing their performance in a matter of days.
Previously, a team led by scientists from the Department of Chemistry at Imperial College, London discovered that this breakdown is due to the formation of ‘superoxide’ that attack the perovskite material. These superoxides are formed when light hitting the cells releases electrons, which react with the oxygen in the air.
Now, in a study published in Nature Communications, the team have determined how the superoxides form and how they attack the perovskite material, and have proposed possible solutions.
Not-so-super oxides
Working with Christopher Eames and Saiful Islam at the University of Bath, the team found that superoxide formation is helped by spaces in the structure of the perovskite normally taken up by molecules of iodide. Although iodide is a component of the perovskite material itself, there are defects where iodide is missing. These vacant spots are then used in the formation of superoxides.
The team found that dosing the material with extra iodide after manufacturing did improve the stability, but that a more permanent solution could be to engineer the iodide defects out.
Lead author of the new study, Nicholas Aristidou from the Department of Chemistry at Imperial, said: “After identifying the role of iodide defects in generating superoxide, we could successfully improve the material stability by filling the vacancies with additional iodide ions. This opens up a new way of optimising the material for enhanced stability by controlling the type and density of defects present.”
Lead researcher Saif Haque from the Department of Chemistry at Imperial added: “We have now provided a pathway to understand this process at the atomic scale and allow the design of devices with improved stability.”
Better solutions
Currently, the only way of protecting perovskite cells from degradation by air and light is to encase them in glass. However, perovskite solar cells are made from flexible material designed to be used in a range of settings, so the glass encasement severely limits their function.
Haque said: “Glass encasement restricts movement and adds weight and cost to the cells. Improving the perovskite cell material itself is the best solution.”
The team hope to next test the stability of the cells in real-world settings. The cells would be exposed to a combination of both oxygen and moisture, testing the cells in more relevant scenarios.
‘Fast oxygen diffusion and iodide defects mediate oxygen induced degradation of perovskite solar cells’ by Nicholas Aristidou et al; Nature Communications 8 15218 (2017)